AISI 4140 moderate hardenability 4140 alloy steel supplier fabrication
More products from this supplier
AISI 4140 Steel Round Bar Sheet Plate, JIS SCM440, DIN 1.7225
· keyword:forged 4140 steel,4140 alloy steel supplier
· Usage: It is used to manufacture forgings that require higher strength and larger quenched and tempered sections than 35CrMo steel, such as large gears for locomotive traction, supercharger transmission gears, rear axles, connecting rods and spring clips that are heavily loaded, and can also be used for Drill pipe joints and fishing tools for oil wells below 2000m, and can be used for molds of bending machines, etc.
· Other Steel Types:5140 /4140 / 4340 / 4142 / 15CrMo / 6150 / 38CrMoAI / 8620 .....
· Serve:OEM/ODM,Sample free and 24 hours online
· Delivery status:With heat treatment (normalized, annealed or high temperature tempered) or without heat treatment Goods, the delivery status should be specified in the contract
AISI 4140 Steel Characteristics
1.It is low alloy steel with chromium, molybdenum, and manganese.
2.Great toughness, fatigue strength, abrasion and impact resistance.
3.It is widely be used in the industry due to its excellent versatility and usefulness.
4.The higher carbon content in it, the higher the strength and heat treatment capabilities it is.
5.It can be oil hardened to relatively high hardenability.
4140 Steel Round Bar Sheet Plate Heat Treatment
At the annealed condition, 1.7225 alloy tool steel has good machinability.
DIN 1.7225 steel has high ductility. It can be formed using conventional techniques in the annealed condition. It is required more pressure or force for forming because it is tougher than plain carbon steels.
1.7225 alloy steel can be welded using all advanced techniques. But, the mechanical properties of it will be affected if it is welded in the heat treated condition, and post weld heat treatment should be performed.
1.7225 tool steel is heated at 845°C(1550°F) followed by quenching in oil. Before hardening, it can be normalized by heating at 913°C (1675°F) for a long period of time followed by air cooling.
It is forged at 926 to 1205°C(1700 to 2200°F)
4140 steel can be hot worked at 816 to 1038°C(1500 to 1900°F)
1.7225 steel can be cold worked using conventional methods in the annealed condition.
Heat it to 800℃ – 850℃, hold until temperature is uniform throughout the section and cool in furnace.
Heat 1.7225 alloy steel to 870℃ – 900℃, hold it until the temperature is uniform throughout the section, soak for 10 – 15 minutes and cool in still air.
DIN 1.7225 steel can be tempered at 205 to 649°C (400 to 1200°F) depending upon the desired hardness level. The hardness of the steel can be increased if it has lower tempering temperature. For example, tensile strength of 225 ksi cab be achieved by tempering at 316°C (600°F), and tensile strength of 130 ksi can be achieved by tempering at 538°C (1000°F).
DIN 1.7225 alloy steel can be hardened by cold working, or heating and quenching.
Dongguan Songshun Mould Steel Co., Ltd. is an Indusrtial and trading company with 2 warehouses that manufactures good & high quality kinds of steels starting from 2012. The company provides the customized products and OEM service. What´s more, we keep the mass stock of over 20000 tons. In those years, we offer a wide range of steels to our customers from all over the world. And we enjoy high praise among them.
|Payment Terms :||L/C, D/A, D/P, T/T, Western Union......|
|Sample Policy :||Yes|
|Packaging Info :||1. Standard export package 2. In bundles with steel strips 3. Meet requirements of customers|
|Delivery Info :||7-30days|
|Model Number :||4140/42CrMo/1.7225/40CD4/SCM440/708M40/G41400|
|Color :||Can be custom|
|Size :||Can be custom|
|Weight :||Can be custom|
|Style :||steel round bar|
|Technology :||Hot Forged +Rough Machined (black Surface|
|Grade :||AISI 4140/ASTM 4140/DIN 1.7225 /NF 40CD4 /JIS SCM440 /GB 42CrMo /BS 708M40|